57% High Translucent 1050 Mpa Dental Zirconia Discs 20mm 22mm 25mm
57% High translucent 1050Mpa zirconia ceramic blocks/discs and ce
zirconia blocks dental for false zirconia blocks dental
Introduction of YUCERA's UT Multilayer high translucent dental
zirconia:
1. Natural color gradient – Efficient fabrication of natural
looking restorations
2. Specially adjusted translucency gradient – Good coverage in the
cervical area and increased translucency in the incisal area
3. High flexural strength – Single-unit restorations up to 3-unit
bridges
It impresses with its perfect balance between translucency and
strength for the production of aesthetic all-ceramic restorations.
The soft material before sintering ensures an effortless
manufacturing process.
Features of 3D Plus/pro Multilayer high translucent strong
zirconium oxide for fixed and implant-supported prosthetics:
1. Outstanding aesthetics – high translucent and high strength.
2. Extensive color selection – 20 colors ( 16 A-D, 3 Bleach).
3. Wide range of indications – from single-tooth restoration to
multi-unit bridge.
4. 700-1050 MPa Bending Strength of zirconia disc.
5. 46-49% Translucency of zirconia disc.
6. High opacity – for discolored stumps;High processing comfort –
easy to mill.
8. Flexibility in processing – for fixed and implant-supported
prosthetics.
Indications
This type block can be used in anterior and posterior single-tooth
restorations and anterior and posterior3-unit bridges and
Multi-unit bridges (anterior and posterior).
Processing Options
1. Monolithic processing or partial ceramic veneering
2. Optional brush or dipping infiltration possible
Colors
A1, A2, A3, A3.5, A4; B1, B2, B3, B4; C1, C2, C3, C4; D2, D3, D4
OM1, OM2, OM3
Packaging
Single Disc
YUCERA all series
| Type | Code | Translucency | Bending Strength | Hardness | Color | Size |
| White zirconia block | HT | 40% | ≧1200Mpa(Av.) | 1200HV | White (coloring liquid with vita 16 shades and 26
shades | Open system& Zirkon zahn system & Amann Girrbach System |
ST
| 43% | ≧1200Mpa(Av.) | 1200HV |
| Preshaded zirconia block | ST-Color | 43% | ≧1100Mpa(Av.) | 1200HV | Vita 16 shades and BL1, BL2, BL3 |
| Multilayer preshaded zirconia block | SHT-ML | 46% | ≧900Mpa(Av.) | 1200HV |
| UT-ML | 49% | ≧600Mpa(Av.) | 1200HV |
| 3D Plus-ML | 43%-57% | ≧700Mpa(Av.)--1050Mpa(Av.) | 1200HV |
Suitable for below system
| Open Cadcam System | Zironzahn System | Amann Girrbach |
| 98x10mm | 95x10mm | / |
| 98x12mm | 95x12mm | AGx12mm |
| 98x14mm | 95x14mm | AGx14mm |
| 98x16mm | 95x16mm | AGx16mm |
| 98x18mm | 95x18mm | AGx18mm |
| 98x20mm | 95x20mm | AGx20mm |
| 98x22mm | 95x22mm | AGx22mm |
| 98x25mm | 95x25mm | AGx25mm |
| SHT Multileyer/UT Multilayer /3D Multilayer Sintering Curve |
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 900 | 90 | 9.7 |
| Step 2 | 900 | 900 | 30 | 0 |
| Step 3 | 900 | 1500 | 180 | 3.3 |
| Step 4 | 1500 | 1500 | 120 | 0 |
| Step 5 | 1500 | 800 | 60 | -11.6 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |