1200HV 3D Plus Dental Zirconia Block False Dental Zirconia Discs
Dental 1500 zirconium blocks and 49 zirconium blocks and ce dental
zirconia blank used in false zirconia blocks
Introduction of YUCERA's 3D Plus Multilayer dental zirconia:
3D plus multilayer zirconia blockis a dental zirconia (Y-TZP ZrO2)
for highly translucent, monolithic restorations. 3D plus multilayer
zirconia block offers with 700-1050MPa an outstanding high flexural
strength combined with high translucency. The soft material before
sintering ensures an effortless manufacturing process. All-ceramic
veneering is possible with the common all-ceramic systems (see CET
value).
Features of 3D Plus Multilayer dental zirconia/ceramics
block/blank/discs:
1. Sintered Density of zirconia disc 6.07 ± 0.03g/cm3
2. Outstanding aesthetics – high translucent and high strength.
3. Translucency of zirconia disc 57-43%
4. Extensive color selection – 19 colors (Blench, A1-D4).
5. Bending Strength of zirconia disc700-1050 MPa
6. Hardness of zirconia disc 1200HV
7. Wide range of indications – from single-tooth restoration to
multi-unit bridge.
8. Vita 16 color of A1-D4 and Blench OM1/2/3 color
9. Self-colored dental zirconia blocks
10. CAD CAM digital system
11. High translucent zirconium oxide for perfect aesthetics
Processing Options
1. Monolithic processing or partial ceramic veneering
2. Optional brush or dipping infiltration possible
Indications
Single-tooth restorations (anterior and posterior)
3-unit bridges (anterior and posterior)
Multi-unit bridges with NexxZr + white (anterior and posterior)
Packaging
Single Disc
YUCERA all series
| Type | Code | Translucency | Bending Strength | Hardness | Color | Size |
| White zirconia block | HT | 40% | ≧1200Mpa(Av.) | 1200HV | White (coloring liquid with vita 16 shades and 26
shades | Open system& Zirkon zahn system & Amann Girrbach System |
ST
| 43% | ≧1200Mpa(Av.) | 1200HV |
| Preshaded zirconia block | ST-Color | 43% | ≧1100Mpa(Av.) | 1200HV | Vita 16 shades and BL1, BL2, BL3 |
| Multilayer preshaded zirconia block | SHT-ML | 46% | ≧900Mpa(Av.) | 1200HV |
| UT-ML | 49% | ≧600Mpa(Av.) | 1200HV |
| 3D Plus-ML | 43%-57% | ≧700Mpa(Av.)--1050Mpa(Av.) | 1200HV |
Suitable for below system
| Open Cadcam System | Zironzahn System | Amann Girrbach |
| 98x10mm | 95x10mm | / |
| 98x12mm | 95x12mm | AGx12mm |
| 98x14mm | 95x14mm | AGx14mm |
| 98x16mm | 95x16mm | AGx16mm |
| 98x18mm | 95x18mm | AGx18mm |
| 98x20mm | 95x20mm | AGx20mm |
| 98x22mm | 95x22mm | AGx22mm |
| 98x25mm | 95x25mm | AGx25mm |
| SHT Multileyer/UT Multilayer /3D Multilayer Sintering Curve |
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 900 | 90 | 9.7 |
| Step 2 | 900 | 900 | 30 | 0 |
| Step 3 | 900 | 1500 | 180 | 3.3 |
| Step 4 | 1500 | 1500 | 120 | 0 |
| Step 5 | 1500 | 800 | 60 | -11.6 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
Our service
1. Yucera establish cooperation with many large denture processing
center and oral hospitals, get outstanding performance in the field
and earn good reputation amount technicians and patients.
2. We have already passed the CE and ISO certification.
I’m sure that our factory is good enough for your program in your
market.
Welcome any comments.