6 Layer Multilayer Dental Zirconia Block For Aesthetic Restoration
6 Layer Multilayer Dental Zirconia Blocks Dental Discs For
Aesthetic Restoration with 43-57% transmittance
Introduction of YUCERA:
1. Top three dental zirconia block/blank/discs manufacturer in
China;
2. Two production lines with output of 60,000.00 blocks per month;
3. More than 100 staffs;
4. White block, pre-shaded block and multilayer block;
Features of 3D Plus Multilayer dental zirconia/ceramics block/blank/discs:
1. Sintered Density of zirconia disc 6.07 ± 0.03g/cm3
2. Translucency of zirconia disc 57-43%
3. Bending Strength of zirconia disc700-1050 MPa
4. Hardness of zirconia disc 1200HV
5. Vita 16 color of A1-D4 and Blench OM1/2/3 color
6. Self-colored dental zirconia blocks
7. CAD CAM digital system
Advantage of 3D Plus Multilayer dental zirconia/ceramics block/blank/discs:
1. High quality zirconia powder
2. Isostatic pressed to ensure homogenous density and shrinkage
distribution.
3. Easy to cut, no porcelain breakage, less scraps
4. More accurate scaling factor
YUCERA all series
| Type | Code | Translucency | Bending Strength | Hardness | Color | Size |
| White zirconia block | HT | 40% | ≧1200Mpa(Av.) | 1200HV | White (coloring liquid with vita 16 shades and 26
shades | Open system& Zirkon zahn system & Amann Girrbach System |
ST
| 43% | ≧1200Mpa(Av.) | 1200HV |
| Preshaded zirconia block | ST-Color | 43% | ≧1100Mpa(Av.) | 1200HV | Vita 16 shades and BL1, BL2, BL3 |
| Multilayer preshaded zirconia block | SHT-ML | 46% | ≧900Mpa(Av.) | 1200HV |
| UT-ML | 49% | ≧600Mpa(Av.) | 1200HV |
| 3D Plus-ML | 43%-57% | ≧700Mpa(Av.)--1050Mpa(Av.) | 1200HV |
Suitable for below system
| Open Cadcam System | Zironzahn System | Amann Girrbach |
| 98x10mm | 95x10mm | / |
| 98x12mm | 95x12mm | AGx12mm |
| 98x14mm | 95x14mm | AGx14mm |
| 98x16mm | 95x16mm | AGx16mm |
| 98x18mm | 95x18mm | AGx18mm |
| 98x20mm | 95x20mm | AGx20mm |
| 98x22mm | 95x22mm | AGx22mm |
| 98x25mm | 95x25mm | AGx25mm |
| SHT Multileyer/UT Multilayer /3D Multilayer Sintering Curve |
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 900 | 90 | 9.7 |
| Step 2 | 900 | 900 | 30 | 0 |
| Step 3 | 900 | 1500 | 180 | 3.3 |
| Step 4 | 1500 | 1500 | 120 | 0 |
| Step 5 | 1500 | 800 | 60 | -11.6 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
Note:
Using different brands of sintering furnaces, different sintering
temperatures and programs,the color and translucent of crown will
be slightly different.Do not use rapid sintering furnace,because
the temperature rise too fast, the zirconia can* t be sintered
completely which will have large affect to the hardness and
translucent of the crown.
FAQ
Q: What about your package?
A: We use standard export packing.To make products safe ,no demage
100%
Q: Do you have guarantee on your products?
A: We guarantee the goods produced is same as standard
ISO13485,CE,FDA
Q: How will you treat quality complaint?
A: First of all, Yucera Has strict quality control, We have
responded to professional inspection before shipment . It will
reduce the possibility of quality problem to near zero. If this is
really a quality problem caused by us we will send you free goods
for replacement, or refund you're the loss.
Q: Is there discount?
A: Sure, different quantity will have different discount.
Q: Can I have sample?
A: Yes, but sample is charged and customers pay freight charge.